Picosecond laser-induced surface structures on alloys in liquids and their influence on nanoparticle productivity during laser ablation

Nadarajah, Ruksan; Barcikowski, Stephan GND; Gökce, Bilal GND

The productivity of nanoparticles formed by laser ablation of gold-silver and iron-gold alloy as well as copper and iron-nickel alloy targets in water is correlated with the formation of laser-induced surface structures. At a laser fluence optimized for maximum nanoparticle productivity, it is found that a binary alloy with an equimolar ratio forms laser-induced periodic surface structures (LIPSS) after ablation, if one of the constituent metals also form LIPSS. The ablation rate of nanoparticles linearly depends on the laser fluence if LIPSS is not formed, while a logarithmic trend and a decrease in productivity is evident when LIPSS is formed. To cancel LIPSS formation and recover from this decrease, a change to circularly polarized light is performed and an increase in nanoparticle productivity of more than 30% is observed.

Cite

Citation style:
Nadarajah, R., Barcikowski, S., Gökce, B., 2020. Picosecond laser-induced surface structures on alloys in liquids and their influence on nanoparticle productivity during laser ablation. https://doi.org/10.1364/OE.28.002909
Could not load citation form.

Rights

License Holder:

© 2020 Optical Society of America under the terms of the OSA Open Access Publishing Agreement https://www.osapublishing.org/library/license_v1.cfm#VOR-OA

Use and reproduction:
All rights reserved

Export